| raw magnets SmCo |
 |
|
|
|
|
magnetized via the height (H)
| Order Number |
grade |
L mm |
B mm |
H mm |
magnetization |
force*N |
weight g |
temperature °C |
| MSAQm7.5x4x1.5 |
RCS20 |
7.5 +0.1/-0.1 |
4 +0.1/-0.1 |
1.5 +0.1/-0.1 |
axially |
3.4 |
0.4 |
200 |
| MSAQm7.5x6x2 |
RCS20 |
7.5 +0.1/-0.1 |
6 +0.1/-0.1 |
2 +0.1/-0.1 |
axially |
5.0 |
0.7 |
200 |
| MSAQm10x7.5x2 |
RCS20 |
10 +0.1/-0.1 |
7.5 +0.1/-0.1 |
2 +0.1/-0.1 |
axially |
7.5 |
1.2 |
200 |
| MSAQm12x9.5x2.5 |
RCS20 |
12 +0.1/-0.1 |
9.5 +0.1/-0.1 |
2.5 +0.1/-0.1 |
axially |
11 |
2.5 |
200 |
| MSAQm16x12x2.5 |
RCS20 |
16 +0.1/-0.1 |
12.5 +0.1/-0.1 |
2.5 +0.1/-0.1 |
axially |
15 |
4 |
200 |
| MSAQm18x16.5x4 |
RCS20 |
18 +0.1/-0.1 |
16.5 +0.1/-0.1 |
4 +0.1/-0.1 |
axially |
29 |
10 |
200 |
| MSAQm26x20.3x5 |
RCS20 |
26 +0.1/-0.1 |
20.3 +0.1/-0.1 |
5 +0.1/-0.1 |
axially |
51 |
22 |
200 |
| MSAQm33x26x6.5 |
RCS20 |
33 +0.1/-0.1 |
26.3 +0.1/-0.1 |
6.5 +0.1/-0.1 |
axially |
85 |
47 |
200 |
*The holding forces have been determined at room temperature on a polished plate made of steel ( S235JR according to DIN 10 025) with a thickness of 10 mm by pulling the magnet vertically from the surface (1kg~10N). A deviation of -10 % (max.) in the stated values is possible in exceptional cases. In general, the value will be exceeded.