Flat pot magnets of hard ferrite

Flat pot magnets of hard ferrite, steel body, with cylinder bore, galvanized

Alternative to the standard we also offer individual solutions:
» Corrosion protection with black galvanised housing surfaces (up to 720 hours in a salt spray test - depending on the magnet material)
Article number D mm H mm d1 mm d2 mm Force* N Weight g Temperature °C  
F50C-v 50+0.2/-0.1 10+0.5/-0.2 8.5+0.2/-0.2 22 180 85 200
F57C-v 57+0.2/-0.1 11+0.5/-0.2 6.5+0.2/-0.2 24 230 130 200
F63C-v 63+0.3/-0.1 14+0.5/-0.2 6.5+0.2/-0.2 24 290 197 200
F80C-vH10L6.4 80+0.3/-0.1 10+0.5/-0.2 6.4+0.2/-0.2 32 450 235 200
F80C-v 80+0.3/-0.1 18+0.5/-0.2 6.5+0.2/-0.2 11.5 540 458 200
F83C-v 83+0.3/-0.1 18+0.5/-0.2 10.5+0.2/-0.2 32 600 444 200
F100C-v 100+0.5/-0.1 22+0.5/-0.2 10.5+0.2/-0.2 34 680 815 200
REACH
RoHS
UV_resistance
PAC free
* The forces have been determined at room temperature on a plate in polished steel (S235JR according to DIN 10 025) with a thickness of 10 mm (1kg ~ 10N). A maximum deviation of -10% compared to the specified value is possible in exceptional cases. Value is exceeded in general. Small cracks in the magnetic material do not influence the force. Depending on the type of application (installation situation, temperatures, counter anchor etc.) the forces can be influenced enormously. The indicated values are serving as an orientation. Please get advice and help from our experts.