Flat pot magnets of hard ferrite, steel body, with internal thread, galvanized
Flat pot magnets of hard ferrite
Flat pot magnets of hard ferrite, steel body, with internal thread, galvanized
Alternative to the standard we also offer individual solutions: » Corrosion protection with black galvanised housing surfaces (up to 720 hours in a salt spray test - depending on the magnet material)
Article number
D mm
H mm
K mm
Thread M
Force* N
Weight g
Temperature °C
F25D-vM4
25+0.1/-0.1
7+0.3/-0.2
5.2
M4
36
18
200
F32D-vM4
32+0.1/-0.1
7+0.3/-0.2
5.2
M4
75
29
200
F40D-vM4
40+0.2/-0.1
8+0.4/-0.2
5.2
M4
90
53
200
F50D-vM6
50+0.2/-0.1
10+0.5/-0.2
12
M6
170
94
200
F50D-vM8
50+0.2/-0.1
10+0.5/-0.2
12
M8
170
94
200
F63D-vM8
63+0.3/-0.1
14+0.5/-0.2
13
M8
290
206
200
F80D-vM8
80+0.3/-0.1
18+0.5/-0.2
14.5
M8
550
472
200
FG080HFD-08v-00 ¹
80+0.3/-0.1
10+0.5/-0.2
12
M8
550
240
200
F80D-vM10
80+0.3/-0.1
18+0.5/-0.2
14.5
M10
550
466
200
¹ Housing punched from strip steel, rear chamfer with radius
* The forces have been determined at room temperature on a plate in polished steel (S235JR according to DIN 10 025) with a thickness of 10 mm (1kg ~ 10N). A maximum deviation of -10% compared to the specified value is possible in exceptional cases. Value is exceeded in general. Small cracks in the magnetic material do not influence the force. Depending on the type of application (installation situation, temperatures, counter anchor etc.) the forces can be influenced enormously. The indicated values are serving as an orientation. Please get advice and help from our experts.